ASTM A269 316 Stainless Steel Tubing, ASTM A213 ASME SA213 TP 316L Stainless Steel Tube, ASTM A312 ASME SA312 TP 316L Stainless Steel Pipe, 316L U bend Tubes, ASME SA 213 TP316 / 316L / ASTM A213 A312 TP316 TP316L EN 10216 – 5 1.4401 / 1.4404 Stainless Steel Tubes. ASTM A213 TP316, A312 TP316L, A213 TP316L, ASME SA213 316L, ASME SA213 TP316L. ASME SA312 TP 316L, 316 Stainless Steel Tube, 316L Stainless Steel Tube, 316 Stainless Steel Tubing, 316L Stainless Steel Tubing, 316 Stainless Steel Pipe, 316L Stainless Steel Pipe, 316 Stainless Steel Tubing, 316L Tubing.
|Outside Diameter:||6 – 508mm (1/8 – 20 Inch)|
|Wall Thickness:||0.50 – 63.5mm (0,02 – 2 1/2 inch)|
|Standard Specification:||EN 10216-5; DIN 17456, DIN 17458, DIN 2462, DIN 17455|
|GB/T14975; T14976; T13296; GB5310;|
|ASTM A213, A269, A312, A511, A789, A790, A928, A999, A1016, ASTM B161, ASTM B163, ASTM B165, ASTM B167, ASTM B338, ASTM B407, ASTM B423, ASTM B444,ASTM B619, ASTM B622, ASTM B626, ASTM B668, ASTM B677, ASTM B829|
|JIS G3459, JIS G3463, JIS G3446, JIS G3447, JIS G3448, JIS G3468|
|GOST 9940;GOST 9941;|
316 Stainless Steel Tubing are molybdenum-bearing austenitic stainless steel, which are more resistant to general corrosion and pitting corrosion, crevice corrosion than the conventional chromium-nickel austenitic stainless steel such as 304. 316L Stainless Steel also offer higher creep, stress-to-rupture, and tensile strength at elevated temperature. The recommended temperature range includes -425°F to 1,200°F (-255°C to 605°C). In addition to excellent corrosion resistance and strength properties, the Alloys 316 and 316L Cr-Ni-Mo alloys also provide excellent fabricability and formability which are typical of the austenitic stainless steel.
316L Stainless Steel Tubing is improved version of 304 Stainless Steel, with the addition of molybdenum and higher nickel content. The resultant Chemical composition of 316 gives the stainless steel much increased corrosion resistance in aggressive environment. Molybdenum make the steel more resistant to pitting and crevice corrosion in chloride-contaminated media, sea water and acetic acid vapour. The lower rate of general corrosion in mildly corrosive environment give the steel good atmospheric corrosion resistance in polluted marine atmosphere, and because of low carbon percentage, can minimizing Intergranular corrosion attact.
316 316L Stainless Steel offers higher strength and better creep resistance at higher temperature than 304. 316L Stainless Steel also possesses excellent mechanical properties and corrosion properties at sub-zero temperatures. When there is a danger of corrosion in the heat affected zones of weldments, the low-carbon variety 316L should be used. 316Ti, the titanium-stabilised version, is used for its resistance to sensitization during prolonged exposure in the 550 °C-800 °C temperature range.
316 316L (2% to 3% Mo) is the most widely used molybdenum-containing stainless steel. It is designated as a tank, pipe and heat exchanger material for food processing and pharmaceutical production. Increased molybdenum content enhances resistance to chloride in the air, so Type 316 can be used as a material of choice for offshore and coastal buildings. 316L is used to cover the Canary Wharf building in London and the tallest building in the world – the outer layer of the Petronas Tower in Kuala Lumpur, Malaysia.
What does the L mean?
L-grades have 0.035% carbon maximum. L-grades are resistant to sensitization in short-term exposures or heat treatments. L-grade often have slightly lower (typically 5,000 psi less) minimum strengths than standard stainless steel.
Chemical Composition ASME SA 213 316 /316L EN 10216-5 1.4401 1.4404
|Carbon (C) Max.||0.08||0.035||0.07||0.030|
|Manganese (Mn) Max.||2.00||2.00||2.00||2.00|
|Phosphorous (P) Max.||0.045||0.045||0.040||0.040|
|Sulphur (S) Max.||0.030||0.030||0.015||0.015|
|Silicon (Si) Max.||1.00||1.00||1.00||1.00|
|Chromium (Cr)||16.0 – 18.0||16.0 – 18.0||16.5 – 18.5||16.5 – 18.5|
|Nickel (Ni)||10.0 – 14.0||10.0 – 14.0||10.0 – 13.0||10.0 – 13.0|
|Molybdenum (Mo)||2.0 – 3.0||2.0 – 3.0||2.0 – 2.5||2.0 – 2.5|
|Nitrogen (N) Max.||–||–||0.015||0.015|
Mechanical Properties of 316/316L/316H Stainless Sreel in the Annealed Condition at -20°F to +100°F
|Alloy||UNS||Spec.||Tensile Strength||Yield Strength||Elongation in 2 inch (min.) %||Grain Size Req.||Max. Hardness HRB Rockwell|
|TP316H||S31609||—||—||—||—||—||—||7 or coarser||—|
AVAILABLE STOCK OF ASTM A213 316L TUBE , ASTM A312 316 316L SS SEAMLESS TUBE
|ASTM A213 TP316 TP316L Stainless Steel Coil Tube Supplier & Manufacturer in China||ASME SA213 316L Stainless Steel Tube Supplier & Manufacturer in China|
|ASTM A312 316 316L Stainless Steel Capillary Tube Supplier & Manufacturer in China||ASTM A312 316 316L Schedule 40 Stainless Steel Pipe Supplier & Manufacturer in China|
|ASTM A312 316 316L Stainless Steel U Bend Tube Supplier & Manufacturer in China||ASME SA213 316L Schedule 80 Stainless Steel Pipe Supplier & Manufacturer in China|
|ASTM A312 316 316L seamless Tubing Supplier & Manufacturer in China||ASTM A312 316 316L Schedule 10 Stainless Steel Pipe Supplier & Manufacturer in China|