Hastelloy C22 round bar
Specification
| Grade | Hastelloy C22 - UNS N06022 - ALLOY C-22 (Ni/ 22Cr/ 13Mo/ 3Fe/ 3W) |
|---|---|
| Specification | ASTM B574 UNS N06022, ASTM B574 / ASME SB574 / AMS 5766 |
| Standard | ASTM, ASME, API, GB, AISI, DIN, EN, SUS, UNS |
| Alloy C22 Round bar size | Diameter: 3-~800mm |
| C22 Hastelloy Hex Bar size | 2-100mm A/F |
| Hastelloy Alloy C22 Flat bar size | Thickness: 2 -100mm |
| Width: 10 to 500mm | |
| C22 Hastelloy Alloy Square bar size | 4 to 100mm |
| Hastelloy C22 Angle bar size (in mm) | 3*20*20~12*100*100 |
| ASTM B574 Hastelloy C22 Section | 3.0 to 12.0mm thickness |
| Hastelloy WERKSTOFF NR. 2.4602 Channel Bar (in mm) | 80 x 40 to 150 x 75 section; 5.0 to 6.0 thickness |
| Nickel Alloy C22 Hollow Bar (in mm) | 32 OD x 16 ID to 250 OD x 200 ID) |
| 2.4602 Hastelloy C22 Billet Size | 1/2" to 495mm Diameter |
| ASTM B574 C22 Hastelloy Rectangles Size | 33 x 30mm to 295 x 1066mm |
| C22 Hastelloy Round Bar Finish | Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black |
| Alloy Hastelloy C22 Round Bar Surface | Bright, Hot Rolled Pickled, Cold Drawn, Sand Blasting Finished, Polished, Hairline |
| Hastelloy C22 round bar Condition | Hardened & tempered, annealed |
| C22 Hastelloy Bar Technique | Hot Rolled, Cold Drawn, Cold Rolled, Forged Round Bar, Rod |
| Hastelloy C22 Din 2.4602 Round Bar Tolerance | H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements |
Hastelloy C22 Round Bars Chemical Composition
| Grade | C | Mn | Si | S | Co | Ni | Cr | Fe | Mo | P |
| Alloy C22 | 0.010 max | 0.50 max | 0.08 max | 0.02 max | 2.50 max | 50.015 min* | 20.00 – 22.50 | 2.00 – 6.00 | 12.50 – 14.50 | 0.02 max |
Hastelloy C22 Round Bars Mechanical Properties
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.69 g/cm3 | 1399 °C (2550 °F) | Psi – 1,00,000 , MPa – 690 | Psi – 45000 , MPa – 310 | 45 % |